1. Production grade

National brand: TA1, TA2, TA3, TA7, TA9, TA10, TC4, TC4ELI, TC6, TC9, TC10, TC11

Us label no. : GR1, GR2, GR3, GR5, GR7, GR12

Ii. Production status

Hot working condition (R)

Cold working state (Y)

Annealed state (M)

Solution state (ST)

Three, manufacturing process

Titanium rod manufacturing process:

Hot forging - Hot rolling - turning (polishing)


Iv. Implementation standards

GB: GB/T2965-2007, GB/T13810, Q/BS5331-91

American standard: ASTM B348, ASTM F136, ASTM F67, AMS4928


Reference standard

1: GB 228 metal tensile test method

2: GB/T 3620.1 titanium and titanium alloy grades and chemical composition

3: GB/T3620.2 Titanium and titanium alloy processed products chemical composition and composition allowable deviation

GB 4698 Methods for chemical analysis of titanium sponge, titanium and titanium alloys


5. Technical requirements

1: The chemical composition of titanium and titanium alloy bars shall comply with the provisions of GB/T 3620.1. When repeated inspection is required, the allowable deviation of chemical composition shall comply with the provisions of GB/T 3620.2.

2: The diameter or side length of hot-working bar and its allowable deviation shall comply with the provisions of Table 1.

3: After hot working, the bar shall be turned (ground) polished and cold rolled, and the allowable diameter deviation of cold drawn bar shall comply with the provisions in Table 2.

4: the roundness of the lathe (ground) polished bar after hot working shall not be greater than half of its dimensional tolerance.

5: The length of the variable length of the processed bar is 300-6000mm, and the length of the annealing bar is 300-2000mm. The length of the fixed or double length should be within the range of the variable length. The allowable deviation of fixed length is +20mm; The length of the double ruler should also be included in the amount of cuts of the bar, each of which should be 5mm. The length of the fixed or double ruler should be indicated in the contract.


Performance and use of titanium alloy rod

As a stable metal, titanium alloy rod has the characteristics of high hardness, low density and good corrosion resistance. Because of these advantages of titanium, we will combine titanium with other metals to make titanium alloy rod, which not only has the original characteristics of titanium, but also has some new characteristics in it.


Titanium alloy rod has high strength, low density and good mechanical properties, corrosion resistance, high stability, etc, but the more stable metal, processing is more difficult, so in the production process of titanium alloy rods is more complex, high cost, so the earliest titanium alloy rod is mainly used in aircraft engine components, and rocket and missile flight parts and so on, In addition, titanium rods are mainly used in the military, scientific research, to make some parts of high strength, corrosion resistance. With the continuous development of science and technology, the cost of titanium alloy rod has been reduced a lot, and it can be used in industry, construction and civil use. For example, titanium wheel bolts and nuts processed by titanium alloy rod are more and more recognized because of their strong corrosion resistance. As the high quality performance of titanium alloy rod is widely recognized and the production technical ability level is increasingly improved, the range of titanium rod products will be more and more widely used in the future.